Wet Process Enamels on Copper in Dry Form for Copper
Wet process enamels have proved over the last few years to be very popular, opening up a whole new range of effects. However, delivery costs can sometimes be prohibitive. The availability of the enamels in dry form overcomes this problem, just requiring the addition of water.
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
High quality Wet Process Enamel in dry form for Copper
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
This is a lead-free enamel
Wet Process Enamel for Copper
W.G. Ball wet process enamel supplied as a dry powder, so you are not paying to ship water. Colors run from 12541 White through the yellows, blues, greens, browns, purple, orange and red to 12558, with 12542 Clear Flux and 12543 Copper Groundcoat. To reach the recommended thickness, mix 8 parts powder to 3 parts water by weight; full instructions are above the listing. Once mixed it sprays, dips or brushes to an even ground coat on copper. Sold in 2, 4, 8 and 16 ounce sizes. The steel version is in Wet Process Enamel for Steel.