Wet Process Enamels on Copper in Dry Form for Steel
Wet process enamels have proved over the last few years to be very popular, opening up a whole new range of effects. However, delivery costs can sometimes be prohibitive. The availability of the enamels in dry form overcomes this problem, just requiring the addition of water.
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
Once a layer of sheet steel groundcoat has been applied to the steel and fired, all other wet process enamels and normal jewellery enamels can be used.
The method of production of the fired trials was as follows:-
The metal was degreased. Sheet steel groundcoat was applied by spraying. The enamels can also be dipped or the enamel applied with a soft brush. The enamel was dried and fired for 3 minutes at 1472F. One coat of wet process white was applied and fired at the same temperature, and then two coats of each colour were applied and fired to give a solid opaque colour. The actual size of the tile is 10cm c 10cm and the gauge of metal was 1.6mm
High quality Wet Process Enamel in dry form for Steel
To achieve our recommended thickness of enamel, put 8 parts by weight of wet process dry powder into a suitable sized container then add 3 parts by weight of boiling water and stir until smooth, leave it to cool down and it is then ready to use. If you prefer, you can vary the powder to water ratio to suit your requirements.
The photographs show the enamels applied direct to degreased copper by spraying. If spraying is used, efficient extraction must be used to remove spray vapour from the work area. The enamels can also be applied either by dipping or with a soft brush. Each photograph shows one and two coats of enamel.The gauge of the copper is 0.9. The actual size of each tile is 6cm x 10cm. Firing time was 3 minutes at 1472F. The copper groundcoat can be used to give an off-white base on which to apply wet process colours. Higher and longer firing of wet process enamels on copper gives very interesting results as the tile colours become tinted with chemicals in the copper base.
This is a lead-free enamel
Wet Process Enamel for Steel
The same W.G. Ball wet process range in dry form, made up for steel, with 12559 Steel Groundcoat in place of the copper version. Colors run 12541 White through the yellows, sky and royal blue, celadon, jade and dark green, the browns, grey, purple, orange and red to 12558. Mix with water — 8 parts powder to 3 parts water by weight for the recommended thickness — then spray, dip or brush an even ground onto sheet or formed steel. Sold in 2, 4, 8 and 16 ounce sizes. The copper version is in Wet Process Enamel for Copper.