The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400F (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
The samples were fired over 18 gauage copper with counter on the back side and Milton Bridge E-5 Black on the front. Firing on white or a different colored background has yielded different color results than what is displayed.
The "circle" sample is underfired "sugar fired" at approximately 1- 1:30 minutes at a maximum temperture of 1400 (textured effect)
The "inverted triangle" was fired at approximately 1 - 1:30 minutes at a maximum temperature of 1500F (fused effect)
This enamel contains lead.
Milton Bridge Shimmer Enamel
Shimmer enamels carry a fine metallic sparkle through the fired glass, so the surface catches the light rather than sitting flat. Each is supplied as a 50 gram packet and named for two things: its base color — dove grey, powder blue, white, light rose, turquoise or green — and its shimmer, which is solar gold, shimmer gold, metallic gold, bronze or icy white. The samples shown above the listing were fired over 18 gauge copper on a Milton Bridge E-5 Black ground, with the firing time and temperature for each given alongside. The rest of the Milton Bridge range is under Milton Bridge Enamel.